UKS DYNAMİC SERIES (-20 °C) SBS DOPED PLASTOMERIC WATER ISOLATION MEMBRANE
 |
It is the APP (Atactic Polypropylene) doped plastomeric water isolation
membranes with fiberglass and polyester felt; both sides are coated on
with polyethylene film or one side coated with polyethylene film the
other side coated with aluminum foil or mineral stone.
Product Description
It is the APP (Atactic Polypropylene) doped plastomeric water isolation membranes with fiberglass and polyester felt; both sides are coated on with polyethylene film or one side coated with polyethylene film the other side coated with aluminum foil or mineral stone.
Usage Areas
It is used in groundwwork bundling, parking, terrace and sloping roofs, balconies, plant stands, garden terrace, concreteflumes, rain gutters and water tanks, ponds, swimming pools and ornamentals against underground waters and used under the coating in wet areas such as kitchne, bathroom etc.
Advantages of the Product
It can be easily applied to different type of surfaces of regions in cold climates because of its high flexibility in its structure.It has high tensile and tear strenghth, resistant to aggressive effects in soil and dilation can be easily used in places such as edges of chimneys and parapet walls.
Surface Preparation
Application ground should be purified from loose pieces, oil and other chemicals and surface defects are repaired with the UKS Repair Mortar. It is recommended to use the UKS Bitumen Emulsion as a liner on the application surface for a healthfully application.
Application
It is fully adhered to the surfaces with blowpipe flame leaving 10 cm of margin at jointing parts and 15 cm of margin at roll finishing parts.
Storage
Rolls must absolutely be stored perpendicularly; rolls should be protected from direct UV and sudden temperature changes, the piercing and cutting operations should not be done after application, used terraces should be protect with floor covering.
It is the APP (Atactic Polypropylene) doped plastomeric water isolation membranes with fiberglass and polyester felt; both sides are coated on with polyethylene film or one side coated with polyethylene film the other side coated with aluminum foil or mineral stone.
Usage Areas
It is used in groundwwork bundling, parking, terrace and sloping roofs, balconies, plant stands, garden terrace, concreteflumes, rain gutters and water tanks, ponds, swimming pools and ornamentals against underground waters and used under the coating in wet areas such as kitchne, bathroom etc.
Advantages of the Product
It can be easily applied to different type of surfaces of regions in cold climates because of its high flexibility in its structure.It has high tensile and tear strenghth, resistant to aggressive effects in soil and dilation can be easily used in places such as edges of chimneys and parapet walls.
Surface Preparation
Application ground should be purified from loose pieces, oil and other chemicals and surface defects are repaired with the UKS Repair Mortar. It is recommended to use the UKS Bitumen Emulsion as a liner on the application surface for a healthfully application.
Application
It is fully adhered to the surfaces with blowpipe flame leaving 10 cm of margin at jointing parts and 15 cm of margin at roll finishing parts.
Storage
Rolls must absolutely be stored perpendicularly; rolls should be protected from direct UV and sudden temperature changes, the piercing and cutting operations should not be done after application, used terraces should be protect with floor covering.
| TECHNICAL FEATURES | METRIC UNIT | STANDARD | C 2000 | C 3000 | C3000 AL | PP 3000 | PP 40 K | PP 40 Y | PP 3000 AL | PP 4000 | PP 50 K | PP 50 Y | PP 4000 AL |
| Bearing (Fiberglass and polyester felt) | gr/m2 | TS 11758-1 | Fiberglass | Fiberglass | Fiberglass | Polyester | Polyester | Polyester | Polyester | Polyester | Polyester | Polyester | Polyester |
| Thickness ± 0.2 | mm | TS EN 1849-1 | 2.0 | 3.0 | 3.0 | 3.0 | 3.5 | 3.5 | 3.0 | 4.0 | 4.5 | 4.5 | 4.0 |
| Temperature Resistance | C | TS 11758-1 | >100 | >100 | >100 | >100 | >100 | >100 | >100 | >100 | >100 | >100 | >100 |
| Cold Bending (Maximum) | C | TS EN 1109 | -20 | -20 | -20 | -20 | -20 | -20 | -20 | -20 | -20 | -20 | -20 |
| Tensile Strength (Height/ Width) | N/5 cm | TS 1908 | 400/300 | 400/300 | 400/300 | 1000/800 | 1000/800 | 1000/800 | 1000/800 | 1000/800 | 1000/800 | 1000/800 | 1000/800 |
| Elongation at Break (Height/ Width) | % | TS 1908 | 2/2 | 2/2 | 2/2 | 40/40 | 40/40 | 40/40 | 40/40 | 40/40 | 40/40 | 40/40 | 40/40 |
| Top Surface Coating - PE Foil | - | TS 11758-1 | Pe | Pe | Al | Pe | Min | Min | Al | Pe | Min | Min | Al |
| Sub-Surface Coating - PE Foil | - | TS 11758-1 | Pe | Pe | Pe | Pe | Pe | Pe | Pe | Pe | Pe | Pe | Pe |
| Roll Sizes | m x m | TS 11758-1 | 1 X 15 | 1 X 10 | 1 X 10 | 1 X 10 | 1 X 10 | 1 X 10 | 1 X 10 | 1 X 10 | 1 X 10 | 1 X 10 | 1 X 10 |