UKS TITANIUM SERIES (-10 °C) APP DOPED PLASTOMERIC WATER ISOLATION MEMBRANE
 |  |
It is the APP (Atactic Polypropylene) doped plastomeric water isolation membranes with fiberglass and polyester felt; both sides are coated on with polyethylene film or one side coated with polyethylene film the other side coated with aluminum foil or mineral stone.
Usage Areas
It is used in groundwork bundling, parking area, terrace and pitched roofs, balconies, plant stands, garden terrace, concrete flumes, eaves trough and concealed gutter, retaining and basement walls, sewage treatment plants and under the coating against artesian in wet areas such as water tanks, ponds, swimming pools and ornamental pools, kitchen, bathroom, wc. .
Advantages of the Product
It is flexible, long-lasting, resistant to the aggressive effects that may occur in the soil, can easily be applied to different types of surfaces and can easily be applied to the details such as dilation, edges of chimney and parapet returns, it has high tensile and breakage stability.
Surface Preparation
Application ground should be purified from loose pieces, oil and other chemicals and surface defects are repaired with the UKS Repair Mortar. It is recommended to use the UKS Bitumen Emulsion as a liner on the application surface for a healthfully application.
Application
It is fully adhered to the surfaces with blowpipe flame leaving 10 cm of margin at jointing parts and 15 cm of margin at roll finishing parts.
Storage and Considerations
Rolls must absolutely be stored perpendicularly; rolls should be protected from direct UV and sudden temperature changes, the piercing and cutting operations should not be done after application, used terraces should be protect with floor covering.
APP KATKILI PLASTOMERİK SU YALITIM MEMBRANI
|
APP DOPED PLASTOMERIC WATER ISOLATION MEMBRANE |
METRIC UNIT |
STANDARD |
C 2000 |
C 3000 |
C3000 AL |
PP 3000 |
PP 40 K |
PP 40 Y |
PP 3000 AL |
PP 4000 |
PP 50 K |
PP 50 Y |
PP 4000 AL |
|
Bearing (Fiberglass and polyester felt) |
gr/m2 |
TS 11758-1 |
Fiberglass |
Fiberglass |
Fiberglass |
Polyester |
Polyester |
Polyester |
Polyester |
Polyester |
Polyester |
Polyester |
Polyester |
|
Thickness ± 0.2 |
mm |
TS EN 1849-1 |
2.0 |
3.0 |
3.0 |
3.0 |
3.5 |
3.5 |
3.0 |
4.0 |
4.5 |
4.5 |
4.0 |
|
Temperature Resistance |
C |
TS 11758-1 |
>120 |
>120 |
>120 |
>120 |
>120 |
>120 |
>120 |
>120 |
>120 |
>120 |
>120 |
|
Cold Bending (Maximum) |
C |
TS EN 1109 |
-10 |
-10 |
-10 |
-10 |
-10 |
-10 |
-10 |
-10 |
-10 |
-10 |
-10 |
|
Tensile Strength (Height/ Width) |
N/5 cm |
TS 1908 |
400/300 |
400/300 |
400/300 |
1000/800 |
1000/800 |
1000/800 |
1000/800 |
1000/800 |
1000/800 |
1000/800 |
1000/800 |
|
Elongation at Break (Height/ Width) |
% |
TS 1908 |
2/2 |
2/2 |
2/2 |
40/40 |
40/40 |
40/40 |
40/40 |
40/40 |
40/40 |
40/40 |
40/40 |
|
Top Surface Coating - PE Foil |
- |
TS 11758-1 |
Pe |
Pe |
Al |
Pe |
Min |
Min |
Al |
Pe |
Min |
Min |
Al |
|
Sub-Surface Coating - PE Foil |
- |
TS 11758-1 |
Pe |
Pe |
Pe |
Pe |
Pe |
Pe |
Pe |
Pe |
Pe |
Pe |
Pe |
|
Roll Sizes |
m x m |
TS 11758-1 |
1 X 15 |
1 X 10 |
1 X 10 |
1 X 10 |
1 X 10 |
1 X 10 |
1 X 10 |
1 X 10 |
1 X 10 |
1 X 10 |
1 X 10 |